WAIT-Rubber repair material
Features and Uses
This product is a two-component, room temperature vulcanization, fast repair adhesive. It has high adhesion strength, simple operation, solvent-free, and good fluidity. It has good filling and pouring properties when it is repaired by pouring method. Safe and convenient to use. It has the characteristics of acid resistance, alkali resistance, oil resistance, aging resistance, etc. It can replace imported products.
This product is mainly used for the repair of belt edge damage and belt surface perforation of wire rope core and fiber core belts. It is also used for repairing longitudinal and transverse tears of conveyor belts, sealing and splicing of joints.
Caution
1, A, B components mixed, should be used within 5 - -10 minutes, otherwise the viscosity increases, and the repair effect is reduced.
2、Do not stir with a wooden stick when mixing the glue and do not contact with water. It should be stored in a cool and dry place under seal. The storage period is one year.
Instructions
1. Use a steel wire beating machine or a wooden file to beat, decontaminate and dry the repaired part and the surrounding 23 cm. The splicing seam should be punched into a "V"-shaped groove. If there is water or the temperature is too low, use an iodine tungsten lamp Bake dry.
2. On the rubber surface of the conveyor belt after drying, apply the rubber surface treatment agent evenly with a brush and wait for it to dry.
3. Pour all component B into component A, use a clean, dry metal rod or screw knife (do not use wooden sticks), and stir in the same direction for 2-3 minutes to mix them evenly.
4. Pour the mixed glue into the damaged repair area to full rubber working surface within 3-5 minutes, and then scrape it flat (the glue should also be poured at 2-3 cm around the repair area), and cure at room temperature 3- -Can be used after 4 hours.
5. If the repaired part is broken, you can use plastic self-adhesive tape to paste under the broken part as a mold. If the hole is too large, you can use a polyethylene plastic plate or iron plate to stick under the hole.
6. If the ambient temperature is lower than 15C or the maintenance time is short, you can use an iodine tungsten lamp to heat 30-40C, and it can be used after curing for 3-4 hours.
7. If the belt joint seam is sealed, it can be used after applying glue for 20-30 minutes and then sticking it on the surface with adhesive tape. If time permits, the longer the curing time, the higher the strength.
.jpg)